LNP™ STAT-KON™ DE003ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KlV1oD_LNP-STAT-KON-DE003ER-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DE003ER is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive. Also known as: LNP* STAT-KON* Compound DC-1003 EM MR Product reorder name: DE003ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.040 to 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.32 to 0.41 | % | ISO 294-4 |
| Flow : 24 hr | 0.040 to 0.13 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8780 | MPa | ASTM D638 |
| -- | 8410 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 110 | MPa | ASTM D638 |
| Break | 109 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.1 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7790 | MPa | ASTM D790 |
| -- | 8040 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 183 | MPa | ASTM D790 |
| -- | 177 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 74 | J/m | ASTM D256 |
| 23°C 2 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.5 | J | ASTM D3763 |
| -- | 3.36 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 146 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siveras™ LX70G50C | Toray Resin Company | LCP | Siveras™ |
| Trovidur® ES-FB | Röchling Engineering Plastics SE & Co. KG | PVC, Rigid | Trovidur® |
| Zytel® PLUS PLS93G35DH1 BK261 | DuPont Performance Polymers | Nylon 6 | Zytel® PLUS |
| Iupiace® TX403 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| VALOX™ K3501 resin | SABIC Innovative Plastics | PBT | VALOX™ |