Wanthane® WHT-1180EC
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | Wanthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K9DawS_WanthaneWHT1180EC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYPE: Polyester-based grade Extrusion grade FEATURES: Excellent mechanical properties, high abrasion resistance, good extrusion stability, good low-temperature flexibility. Applications: Wire & cable, spiral tubes, conveyor belt, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| DIN Abrasion | 80.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.00 | MPa | ASTM D412 |
| 300% strain | 9.00 | MPa | ASTM D412 |
| Tensile Strength (Break) | 32.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 160 | % | ASTM D412 |
| Tear Strength | 90.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 24 hr | 18 | % | ASTM D395 |
| 70°C, 22 hr | 50 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -45.0 | °C | ASTM D3418 |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 195 | °C | |
| Mold Temperature | 23 | °C | |
| Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 175 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Adapter Temperature | 195 | °C | |
| Die Temperature | 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIPEX® LG2 | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| Titacon® EX910 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Bergamid™ BG6600-8053 HI HS BK001 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Ferro PP TPP20AE61HB | Ferro Corporation | PP Homopolymer | Ferro PP |
| ICORENE® N9306 | ICO Polymers EMEA, A Division of A. Schulman | Acetal (POM) Copolymer | ICORENE® |