SABIC® PPcompound 5405
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g2WT1P_SABIC-PPcompound-5405.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 5405 is a modified polypropylene compound. Material properties include excellent flow, high impact and good stiffness. The material exhibits excellent esthetical behaviour with very low tiger stripes visibility. Typical applications include automotive exterior parts such as large complex shaped bumpers and trims which can be painted, partialy painted or unpainted. SABIC® PPcompound 5405 is a designated automotive grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.2 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 18.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 300 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 8.0 | kJ/m² | |
| 0°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 140 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 9.0E-5 | cm/cm/°C | |
| 23 to 80°C | 1.3E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K4535 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Electrafil® TPX-PC-02071 | Techmer Engineered Solutions | PC | Electrafil® |
| Hostacom TRC 104N G73024 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Petlon R-Prime B2-G50-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |
| LNP™ THERMOTUF™ VF003 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |