Lustran® ABS 266
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IR7Wbf_Lustran-ABS-266.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS 266 resin is a clear injection molding grade of ABS (acrylonitrile butadiene styrene). This transparent, general-purpose grade provides clarity and toughness with ease of processing. The resin is available in transparent tint, color code 000000. A tough, transparent grade of ABS, Lustran ABS 266 resin is used in housings, toys, lawn and garden applications, and various consumer goods. As with any product, use of Lustran ABS 266 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Specific Volume | 0.930 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1970 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 37.2 | MPa | ASTM D638 |
| Fracture | 29.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 48 | % | ASTM D638 |
| Flexural Modulus | 1770 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 86.7 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm | 93.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 72.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 82.2 | °C | ASTM D648 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 50.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 50.0 | °C | UL 746 |
| RTI (1.50 mm) | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Clear | HB | UL 94 | |
| 3.00 mm, Clear | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.520 | ASTM D542 | |
| Transmittance (2540 µm) | 86.0 | % | ASTM D1003 |
| Haze (2540 µm) | 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 193 - 221 | °C | |
| Middle Temperature | 199 - 227 | °C | |
| Front Temperature | 204 - 232 | °C | |
| Nozzle Temperature | 204 - 232 | °C | |
| Processing (Melt) Temp | 204 - 232 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 34.5 - 82.7 | MPa | |
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 | RTP Company | Nylon 66 | RTP |
| Bergamid™ PA6-MW30 GR002 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| APEX® 65002 | Teknor Apex Company | PVC, Flexible | APEX® |
| Infino TK-4046H | SAMSUNG SDI CO., LTD. | PPA | Infino |
| Sylvin 9077-70 Blue 8358 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |