ALCUDIA® LDPE 2212FG
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | INgvK9_ALCUDIA-LDPE-2212FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 2212FG is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown film applications This material offers easy processability and good balance of mechanical and optical properties. It contains slip (erucamide), antioxidant and antiblock additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 160 to 190°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.15 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 26.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 500 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 140 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, blown film | 4.0 | N | ISO 6383-2 |
| TD : 40 µm, blown film | 2.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 85 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 40 µm thickness film, blow up ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1399 X 128637 B | RTP Company | PPS | RTP |
| TOTAL Polyethylene Lumicene® M 1810 EP | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| AKROMID® B3 ICF 40 black (5020) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| KOPA® KN333HI2 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Kepamid® 2350GFH | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |