Mold Max® 15T
| Category: | Silicone , Silicone |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Mold Max® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f0prxi_Mold-Max-15T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mold Max® 10T, 15T and 27T silicone are water white translucent tin cured silicone rubber compounds that have exceptional tear strength and working properties. They feature Smooth-On's "Libra®" catalyst for long library life. Mixed 100A:10B by weight, vacuum degassing is recommended for de-airing. Rubber cures overnight at room temperature. Similar in appearance to Smooth-On's premium Dragon Skin® platinum silicones, Mold Max® ‘T' silicones are a less costly alternative for creating animatronic skin effects. Mold Max® ‘T' silicones can be thickened with Thi-Vex® ii thickener for brush-on application and effects. An infinite number of color effects can be achieved by adding Silc Pig® silicone pigments or Cast Magic® effects powders. Mold Max® ‘T' series silicones are also good for making molds used for casting plaster and wax. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.925 | cm³/g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 100A:10B by weight | ||
| Operating Temperature | -54 to 204 | °C |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.20 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 15 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.241 | MPa | ASTM D412 |
| Tensile Strength (Break) | 3.38 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength 1 | 16.5 | kN/m | ASTM D624 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | > 20 | kV/mm | ASTM D149 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life | 45 to 55 | min | |
| Thermoset Mix Viscosity | 20000 | cP | ASTM D2393 |
| Demold Time | 1400 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC10P200-767UVBG | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Vydyne® 21Z | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ALCOM® PA66 910/1 GF30 PTFE15 SI2 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Hostalen PP XN125-P | LyondellBasell Industries | PP Random Copolymer | Hostalen |
| Magnobond 108-059 | Magnolia Plastics, Inc. | Epoxy | Magnobond |