GLAMIDE® T-663G50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hwsm7M_GLAMIDE-T-663G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE® T-663G50 is a Polyamide 66 (Nylon 66) product filled with 50% glass fiber. It is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.57 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 4.0 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 to 0.40 | -- | % | |
| 3.00 mm | 0.60 to 0.80 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.40 | -- | % | |
| Equilibrium, 65% RH | 1.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 280 | 250 | MPa | |
| Yield, 23°C | 215 | 160 | MPa | |
| Yield, 80°C | 145 | 115 | MPa | |
| Tensile Elongation (Break, 23°C) | 2.0 | 2.2 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 14000 | 13000 | MPa | |
| 23°C | 12500 | 10000 | MPa | |
| 80°C | 7900 | 6600 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 335 | 310 | MPa | |
| Yield, 23°C | 305 | 260 | MPa | |
| Yield, 80°C | 210 | 175 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 110 | 120 | J/m | |
| 23°C | 150 | 180 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 262 | -- | °C | |
| 1.8 MPa, Unannealed | 255 | -- | °C | |
| CLTE - Flow | 1.9E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 28 | 21 | kV/mm | ASTM D149 |
| Arc Resistance | 100 | 93.0 | sec | ASTM D495 |
| Comparative Tracking Index | 550 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 to 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycast XHA | Cast Nylons Ltd. | Nylon 6 | Nycast |
| ALTECH® PA66 A 3020/100 GB20 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| KOPELEN J-360 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Jamplast JPGPPSHH | Jamplast, Inc. | PS (GPPS) | Jamplast |
| LNP™ VERTON™ RX89047 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |