Polifil® PP M-20
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HiagoG_Polifil-PP-M-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® M series compounds are homopolymer polypropylene resins reinforced with mica. They combine an improved range of high-stiffness values with low mold shrinkage. These compounds are used in large area broad span applications where high modulus values are required and retained. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2480 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 8.0 | % | |
| Flexural Modulus - Tangent (23°C) | 3190 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 42.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 51 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 0.678 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 127 | °C | |
| 1.8 MPa, Unannealed | 82.2 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 104 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Nozzle Temperature | 227 to 232 | °C | |
| Processing (Melt) Temp | 204 to 260 | °C | |
| Mold Temperature | 10.0 to 26.7 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® AR205 | Covestro - Polycarbonates | PC+PET | Makroblend® |
| Mecoline S RDX 1216 F | Melos GmbH | TP, Unspecified | Mecoline |
| Calprene® H6144 | Dynasol Elastomers | SEBS | Calprene® |
| Axiall PVC 8652 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Sylvin 8230-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |