TECACOMP® POM TRM natural 3758
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HTtfTh_TECACOMPPOMTRMnatural3758.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | |
| Apparent Density | 0.68 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 2.5 | % | ISO 294-4 |
| Flow | 2.8 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/50 |
| Tensile Stress | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 25 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| Glass Transition Temperature | -60.0 | °C | DIN 53765 |
| Melting Temperature | 175 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity 1 | 0.30 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| -- | > -30 | °C | |
| long term | °C | ||
| short term | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.6E+13 | ohms | DIN EN 61340 |
| Volume Resistivity | 4.5E+15 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 80 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1840P | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Teflon® PTFE 613A X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| TEREZ PA 6 7200 H | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Braskem PP 6D43 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| FORMOCON® FM350 | Formosa Plastics Corporation | Acetal (POM) Copolymer | FORMOCON® |