LNP™ LUBRICOMP™ RFL34 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HG3lGm_LNP-LUBRICOMP-RFL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4034 Product reorder name: RFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.3 | % | |
| Across Flow : 24 hr | 1.9 | % | |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 8060 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 158 | MPa | ASTM D638 |
| Yield | 155 | MPa | ISO 527-2 |
| Break | 158 | MPa | ASTM D638 |
| Break | 155 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 3.3 | % | |
| Break | 3.3 | % | |
| Flexural Modulus | |||
| -- | 6890 | MPa | ASTM D790 |
| -- | 7000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 221 | MPa | ASTM D790 |
| -- | 223 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.60 | ||
| vs. Itself - Static | 0.60 | ||
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 68 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.2 | J | ASTM D3763 |
| -- | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 262 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 262 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 250 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH2800 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Bayblend® FR3210 TV | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| ALTECH® PP-H A 3020/100 GB20 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Geon™ Vinyl Flexible B6DB1 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| InnoPlus HD6000F | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |