Axiall PVC 18840
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Axiall PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0hmhqW_Axiall-PVC-18840.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-lead stabilized 105C jacket compound for use in SPTO, SJTO and SVTO applications. Best suited for 30 mil walls and larger. |
| General Information | |
|---|---|
| Uses |
|
| Wire Types |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 16.5 | MPa | |
| 100% Strain | 9.48 | MPa | |
| Tensile Elongation (Break) | 340 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Tensile Elongation | UL 1581 | ||
| 60°C, 762.0 µm 1 | 82 | % | |
| Air Aging, 7 days : 136°C, 762.0 µm | 82 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -25.0 | °C | ASTM D746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 26 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 185 | °C |
| Note Message | |
|---|---|
| 1 . | Oil Aging, 7 days, IRM 902 Oil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-8000-GF20 | QTR, Inc. | PBT | QR Resin |
| Tenite™ Butyrate 565A3720023 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| STERLENE™ BMV212W | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| SuperLite® SL552000-100 (2.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Braskem PE SGF4960 | Braskem | HDPE | Braskem PE |