Radel® R-5000

Category:	PPSU , Polyphenylsulfone
Manufacturer:	Solvay Specialty Polymers
Trademark:	Radel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Gsx5HH_Radel-R-5000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Radel® R-5000 is a transparent polyphenylsulfone (PPSU) which offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins. This resin also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties.

Clear: Radel® R-5000 CL 301

Natural: Radel® R-5000 NT

General Information
Features	Acid Resistant Autoclave Sterilizable Base Resistant Biocompatible Detergent Resistant E-beam Sterilizable Ethylene Oxide Sterilizable Flame Retardant General Purpose Good Chemical Resistance Good Dimensional Stability Good Electrical Properties Good Sterilizability Good Thermal Aging Resistance Good Thermal Stability Heat Sterilizable High ESCR (Stress Crack Resist.) High Heat Resistance Hydrolytically Stable Radiation (Gamma) Resistant Radiation Sterilizable Radiotranslucent Steam Resistant Steam Sterilizable Ultra High Toughness
Uses	Automotive Applications Dental Applications Food Service Applications Hospital Goods Medical Devices Medical/Healthcare Applications Membranes Surgical Instruments
Agency Ratings	FAA FAR 25.853a ISO 10993 NSF 51 3 NSF 61 4
RoHS Compliance	RoHS Compliant
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Blow Molding Extrusion Film Extrusion Injection Molding Machining Profile Extrusion Sheet Extrusion Thermoforming
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.29	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (365°C/5.0 kg)	14 to 20	g/10 min	ASTM D1238
Molding Shrinkage - Flow (3.18 mm)	0.70	%	ASTM D955
Water Absorption			ASTM D570
24 hr	0.37	%
Equilibrium	1.1	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (3.18 mm)	2340	MPa	ASTM D638
Tensile Strength (3.18 mm)	69.6	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield, 3.18 mm	7.2	%
Break, 3.18 mm	60 to 120	%
Flexural Modulus (3.18 mm)	2410	MPa	ASTM D790
Flexural Strength (5.0% Strain, 3.18 mm)	91.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	690	J/m	ASTM D256
Tensile Impact Strength (3.18 mm)	399	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm)	207	°C	ASTM D648
Glass Transition Temperature	220	°C	ASTM E1356
CLTE - Flow (3.18 mm)	5.6E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	9.0E+15	ohms·cm	ASTM D257
Dielectric Strength			ASTM D149
0.0254 mm	> 200	kV/mm
3.18 mm	15	kV/mm
Dielectric Constant (3.18 mm, 60 Hz)	3.44		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹(0.762 mm)	V-0		UL 94

Optical	Nominal Value		Test Method
Refractive Index	1.672		ASTM D542

Additional Information	Nominal Value	Unit
Steam Sterilization - w/ Morpholine ²	> 1000	Cycles

Injection	Nominal Value	Unit
Drying Temperature	149	°C
Drying Time	2.5	hr
Processing (Melt) Temp	360 to 391	°C
Mold Temperature	138 to 163	°C
Screw Compression Ratio	2.2:1.0

Extrusion	Nominal Value	Unit
Drying Temperature	171	°C
Drying Time	4.0	hr
Cylinder Zone 1 Temp.	338 to 388	°C
Cylinder Zone 2 Temp.	338 to 388	°C
Cylinder Zone 3 Temp.	338 to 388	°C
Cylinder Zone 4 Temp.	338 to 388	°C
Cylinder Zone 5 Temp.	338 to 388	°C
Adapter Temperature	327 to 371	°C
Melt Temperature	343 to 399	°C
Die Temperature	327 to 371	°C

Note Message
1 .	These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions.
2 .	Cycles passed without cracking, crazing, or rupture.Steam Autoclave Conditions:- Temperature: 270°F (132°C)- Time: 30 minutes/cycle- Steam Pressure: 27 psig (0.19 MPa)- Stress Level: 1000 psi (7.0 MPa) in flexure- Additive: Morpholine at 50 ppm

Resin Grade	Manufacturer	Category	Trademark
Moplen EP540V	LyondellBasell Industries	PP Impact Copolymer	Moplen
Dialon 712	DTR S.r.l. (Develop Thermoplastic Resins)	PC	Dialon
Leona™ CR301	Asahi Kasei Chemicals Corporation	Nylon 66	Leona™
Sarlink® TPE ML-1660N NAT (PRELIMINARY DATA)	Teknor Apex Company	TPE	Sarlink® TPE
Sarlink® TPV X6180N	Teknor Apex Company	TPV	Sarlink® TPV