Monprene® OM-10165
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rewZbc_Monprene-OM-10165.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Monprene OM-10165 is designed for overmolding applications like grips and anti-skid parts for consumer products. Monprene OM-10165 is an opaque grade that exhibits excellent adhesion to nylon. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 67 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 2.32 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 3.04 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 3.67 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 4.81 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 5.32 | MPa | ASTM D412 |
| Flow : Fracture | 5.50 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 520 | % | ASTM D412 |
| Flow : Fracture | 440 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 29.2 | kN/m | ASTM D624 |
| Flow | 30.6 | kN/m | ASTM D624 |
| Compression Set 8 | ASTM D395B | ||
| 23°C, 22 hr | 29 | % | ASTM D395B |
| 70°C, 22 hr | 22 | % | ASTM D395B |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to Nylon |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 - 232 | °C | |
| Middle Temperature | 227 - 249 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 266 - 277 | °C | |
| Processing (Melt) Temp | 266 - 277 | °C | |
| Mold Temperature | 23.9 - 60.0 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 120W | SABIC Americas, Inc. | LLDPE | SABIC® LLDPE |
| Xuchuan 6170/B-8280 (Mid-sole) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| HiFill® MD POM 0167 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Karina CLEAR PVC COMPOUND 80/223-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petlon R-Prime A2-G50-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |