Baytec® MP-090 (BDO)
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GgKIPF_Baytec-MP-090-BDO-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec MP-090 is a modified diphenylmethane diisocyanate (MDI)-terminated polyether prepolymer based on polypropylene ether glycol (PPG). This prepolymer is used in the manufacture of cast polyurethane elastomers. As with any product, use of Baytec MP-090 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 90.0 | mg | ASTM D4066 |
| Compression Deflection | ASTM D575 | ||
| 10% | 1.90 | MPa | ASTM D575 |
| 15% | 2.90 | MPa | ASTM D575 |
| 2% | 0.276 | MPa | ASTM D575 |
| 20% | 3.96 | MPa | ASTM D575 |
| 25% | 5.17 | MPa | ASTM D575 |
| 5% | 0.896 | MPa | ASTM D575 |
| 50% | 16.3 | MPa | ASTM D575 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 6.83 | MPa | ASTM D412 |
| 200% strain | 10.9 | MPa | ASTM D412 |
| 300% strain | 19.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 34.5 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 410 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 63.0 | kN/m | ASTM D624 |
| Cracking | 16 | kN/m | ASTM D1938 |
| Compression Set (70°C, 22 hr) | 45 | % | ASTM D395 |
| Bayshore Resilience | 20 | % | ASTM D2632 |
| Additional Information |
|---|
| Appearance: Pale yellow liquidNCO: 8.95 to 9.24 wt%Specific Gravity at 80°C: 1.07Specific Gravity at 100°C: 1.06Viscosity at 80°C: 255 mPa-sViscosity at 100°C: 115 mPa-sNCO/OH Ratio: 1.05Stoichiometry: 95% TheoryPrepolymer Temperature: 80 to 90°CExtender Temperature: 25 to 70°CMold Temperature: 90 to 110°CPot Life: 4.7 minDemold: 45 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® W 2320 003 PRO | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Nymax™ GMF 604 40 UV Black 115 1 X 1 | PolyOne Corporation | Nylon 6 | Nymax™ |
| Evoprene™ HP 3704 | AlphaGary | SBC | Evoprene™ HP |
| Karina WHITE PVC COMPOUND 851-10/127-Y-ERYB-AS-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/12 GF30 TS15 BK | Techmer Engineered Solutions | Nylon 6/12 | Plaslube® |