Order Products : sales@su-jiao.com
DOWLEX™ 2078G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FzuKAr_DOWLEX-2078G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Resistance (20 µm) | 14.5 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 20 µm | 80.5 | J/cm³ | ASTM D882 |
| TD : 20 µm | 95.5 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 20 µm | 181 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 203 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 10.3 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 11.2 | MPa | ASTM D882 |
| MD : Break, 20 µm | 39.4 | MPa | ASTM D882 |
| TD : Break, 20 µm | 31.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 470 | % | ASTM D882 |
| TD : Break, 20 µm | 660 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 230 | g | ASTM D1922 |
| TD : 20 µm | 610 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.3 µm) | 58 | ASTM D2457 | |
| Haze (20.3 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 218 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：MC-4 阻隔 模具间隙：40 密尔 (1 mm) 熔体温度：425°F (218°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：85 rpm 冷冻线高度：20 英寸 (508 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS SAN-82TR | Polymer Technology and Services, LLC | SAN | PTS |
| VINIKA® CE70DG | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| XENOY™ HX5600HP resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | XENOY™ |
| DENISTAT N 00U 05 ST | Vamp Tech | Nylon 6 | DENISTAT |
| OmniTech™ HIPS SI5 | OMNI Plastics, LLC | PS (HIPS) | OmniTech™ |