IROGRAN® A 95 E 4861
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FuG3sk_IROGRAN-A-95-E-4861.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 95 E 4861 is a high performance polyester based thermoplastic polyurethane intended for extrusion applications. IROGRAN A 95 E 4861 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of extruded films. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.22 | g/cm³ | ASTM D792, DIN 53479 |
| Melt Mass-Flow Rate (MFR) (215°C/21.6 kg) | 45 | g/10 min | |
| Molding Shrinkage - Flow (Injection Molded) | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, Injection Molded | 98 | ASTM D2240 | |
| Shore D, Injection Molded | 54 | ASTM D2240, DIN 53505 | |
| Shore A, Injection Molded | 96 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | |||
| -- | 27 | mm³ | DIN 53516 |
| -- | 26 | mm³ |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain | 14.3 | MPa | ASTM D412 |
| 100% Strain | 14.0 | MPa | DIN 53504 |
| 300% Strain | 22.8 | MPa | ASTM D412 |
| 300% Strain | 26.0 | MPa | DIN 53504 |
| Tensile Strength 4 | |||
| Break | 40.0 | MPa | ASTM D412 |
| Break | 55.0 | MPa | DIN 53504 |
| Tensile Elongation 5 | |||
| Break | 550 | % | ASTM D412 |
| Break | 530 | % | DIN 53504 |
| Tear Strength 6 | |||
| -- | 158 | kN/m | ASTM D624 |
| -- | 120 | kN/m | ISO 34-1 |
| Compression Set 7 | ASTM D395, ISO 815 | ||
| 23°C, 70 hr | 30 | % | |
| 70°C, 24 hr | 46 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 200 to 215 | °C | |
| Cylinder Zone 2 Temp. | 200 to 215 | °C | |
| Cylinder Zone 3 Temp. | 200 to 215 | °C | |
| Cylinder Zone 4 Temp. | 200 to 215 | °C | |
| Cylinder Zone 5 Temp. | 200 to 215 | °C | |
| Adapter Temperature | 200 to 215 | °C | |
| Die Temperature | 200 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® FG42L NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| AKROMID® B3 GK 30 natural (3057) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| KEP® 070P | Kumho Polychem Co., Ltd. | EPM | KEP® |
| LEXAN™ FXEMPX2 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina REDDY BROWN MB (SP31455) -E 36/209-GIN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |