Staramide RF005Z
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iVdfmo_Staramide-RF005Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide RF005Z is a 25 % Glass Fiber Reinforced Polyamide 66 Extrusion Resin (Also know as Staramide RF1005E-BK82205) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 6600 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 232 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XENOY™ HX5600HP resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |
| Evoprene™ COGEE 626 | AlphaGary | SEBS | Evoprene™ COGEE |
| EVALENE® HDPE HJ30541 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| GLS Acetal VG59 | GLS Polymers Pvt. Ltd. | Acetal (POM) Copolymer | GLS Acetal |
| Karina BLACK PVC -E 810D48/1-C-AC-AS-LMP (034128-00) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |