TOTAL Polyethylene XSene® HDPE BM 593
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FafpYK_TOTAL-Polyethylene-XSene-HDPE-BM-593.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HDPE BM 593 is a new generation of bimodal high density polyethylene and is produced by Total Petrochemicals Double Loop Technology TM. HDPE BM 593 has been especially designed for applications where high film rigidity is required. Very thin films can also be easily achieved. HDPE BM 593 is an ideal partner for applications such as food packaging, carrier bags, refuse bags, industrial packaging, hygiene packaging. HDPE BM 593 is a grade to be used for thin films requiring high rigidity and high heat resistance. Good blendability with LDPE, LLDPE & mPE in co-extrusion structures. HDPE BM593 is a high density polyethylene (HDPE) with outstanding stiffness and Environmental Stress Crack Resistance (ESCR). It has been specifically designed for the manufacture of blow moulded packaging for household, industrial, cosmetics liquids with an optimized weight. HDPE BM593 is a pellet grade and contains antioxidants. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.27 | g/10 min | |
| 190°C/21.6 kg | 26 | g/10 min | |
| Environmental Stress-Cracking Resistance (100% Antarox, F50) | > 250 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1350 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 12 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 12 µm, Blown Film | 29.0 | MPa | |
| TD : Yield, 12 µm, Blown Film | 32.0 | MPa | |
| MD : Break, 12 µm, Blown Film | 64.0 | MPa | |
| TD : Break, 12 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 12 µm, Blown Film | 610 | % | |
| TD : Break, 12 µm, Blown Film | 630 | % | |
| Dart Drop Impact (12 µm, Blown Film) | 44 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 12.0 µm | 7.0 | kN/m | |
| TD : 12.0 µm | 233.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1970 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Zeoforte® ZSC 2395 | Zeon Chemicals L.P. | NBR | Zeoforte® |
| ExxonMobil™ NTX 101 | ExxonMobil Chemical | LLDPE | ExxonMobil™ |
| K-vinyl 20 A 74 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Sylvin 5409-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |