Tecnoprene® HK3D NAT003
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FXKasQ_Tecnoprene-HK3D-NAT003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Detergent resistant polypropylene homopolymer reinforced with 15% chemically coupled glass fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.90 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Ash Content | 15 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 62.0 | MPa | ASTM D638 |
| Flexural Modulus | 3400 | MPa | ASTM D790 |
| Flexural Strength | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 137 | °C | ASTM D648 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.30 | ASTM D150 | |
| Comparative Tracking Index | 650 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 210 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 240 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL UW300 - 8229 | AD majoris | Nylon 66 | VENYL |
| Trexlink™ 6760 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| 3M™ Dyneon™ Fluoroplastic FEP 6322Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| EMOPLEN® A 1509 R G3 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| 3M™ Dyneon™ Fluoroelastomer MIP 8640X | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |