LNP™ THERMOCOMP™ AX06437 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FWZKfs_LNP-THERMOCOMP-AX06437-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AX06437 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable. Also known as: LNP* THERMOCOMP* Compound AX06437 Product reorder name: AX06437 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 | % | |
| Across Flow : 24 hr | 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.22 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.32 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3190 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 37.5 | MPa | ASTM D638 |
| Yield | 36.9 | MPa | ISO 527-2 |
| Break 3 | 34.1 | MPa | ASTM D638 |
| Break | 33.8 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield 4 | 1.8 | % | ASTM D638 |
| Yield | 1.9 | % | ISO 527-2 |
| Break 5 | 6.9 | % | ASTM D638 |
| Break | 7.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3060 | MPa | ASTM D790 |
| -- | 3010 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 64.1 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 92.2 | MPa | ASTM D790 |
| Flexural Strain at Break 8 | 64 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 9 | 3.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 290 | J/m | ASTM D4812 |
| 23°C 10 | 22 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 86.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 87.5 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -30 to 30°C | 8.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 2.75 | ASTM D150 | |
| Dissipation Factor (1.00 GHz) | 2.4E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2 mm/min |
| 9 . | 80*10*3 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 MG 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| Network Polymers PP PPB 25 0202 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Jam PE 22502 | Jam Petrochemical Company | LLDPE | Jam PE |
| Sylvin 9077-90 Grey 9604 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Styropek® BF 495 | Styropek S.A. de C.V. | PS (EPS) | Styropek® |