Chemlon® AT10 Datasheet,Nylon 66,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
AT10 is a modified nylon 66 that offers ultra high impact strength coupled with good rigidity, with this impact resistance maintained at sub-zero temperatures. The excellent impact performance also means that it may be possible to use mouldings prior to any conditioning.

General Information
Features	Ultra-high impact resistance Rigidity, high Low temperature impact resistance
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.09	--	g/cm³	ISO 1183
Molding Shrinkage ¹	2.0 - 2.4	--	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	2.1	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	1800	1500	MPa	ISO 527-2
Tensile Stress (Yield)	48.0	42.0	MPa	ISO 527-2
Flexural Modulus	1800	1100	MPa	ISO 178
Flexural Stress ²	53.0	30.0	MPa	ISO 178

Impact	Dry	Conditioned	Test Method
Charpy Notched Impact Strength	50 kJ/m²	No Break	ISO 179
Charpy Unnotched Impact Strength	No Break	No Break	ISO 179
Notched Izod Impact	80 kJ/m²	No Break	ISO 180
Unnotched Izod Impact Strength	No Break	No Break	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	150	140	°C	ISO 75-2/B
1.8 MPa, not annealed	70.0	60.0	°C	ISO 75-2/A

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+12	1.0E+11	ohms	IEC 60093
Volume Resistivity	1.0E+13	1.0E+13	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	10	12	kV/mm	IEC 60243-1
Relative Permittivity (1 MHz)	3.10	--		IEC 60250
Comparative Tracking Index	> 600	> 600	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating	HB	--		Internal method
Oxygen Index	21	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	80.0 - 100	°C
Drying Time	2.0	hr
Rear Temperature	265 - 285	°C
Middle Temperature	265 - 285	°C
Front Temperature	265 - 285	°C
Processing (Melt) Temp	< 300	°C
Mold Temperature	20.0 - 40.0	°C
Injection Rate	Moderate
Screw Speed	50 - 200	rpm

Injection instructions
Back pressure: LowInjection pressure: MediumNo drying is necessary unless the materials has been exposed to air for longer than three hours.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .	At conventional deflection

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

2 .

At conventional deflection

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FP4Z5z_Chemlon-AT10.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Purell PE 2420 F	LyondellBasell Industries	LDPE	Purell
TechnoFiber PP LGF50-10 HI	TechnoCompound GmbH	PP, Unspecified	TechnoFiber
VENELENE® 11O4	Poliolefinas Internacionales, C.A. (Polinter)	LLDPE	VENELENE®
ALFATER XL® A65E 2GP0000	ALBIS PLASTIC GmbH	TPV	ALFATER XL®
Ferro PP LPP40BK09BK	Ferro Corporation	PP, Unspecified	Ferro PP