VENELENE® 11O4
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark: | VENELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qrG1lK_VENELENE-11O4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 35 | µm | |
| Film Puncture Force (35 µm) | 9.02 | N | ASTM D3420 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 35 µm | 47.0 | MPa | ASTM D882 |
| TD : Fracture, 35 µm | 41.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 35 µm | 720 | % | ASTM D882 |
| TD : Fracture, 35 µm | 810 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 35 µm | 1000 | g | ASTM D1922 |
| TD : 35 µm | 850 | g | ASTM D1922 |
| Impact Resistance, Film | 500 | J/cm | ASTM D1709 |
| Toughness, Film | ASTM D882 | ||
| MD | 130 | MPa | ASTM D882 |
| TD | 150 | MPa | ASTM D882 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (35.0 µm) | 80.0 | % | ASTM D1003 |
| Haze (35.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 210 | °C |
| Extrusion instructions |
|---|
| Inverted Extrusion profile (descendent). Blow up ratio (BUR): 2 - 3. Die gap: 0.9 a 1.5 mm. Frost line Height: 4 - 5 times Die Diameter. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® GM3800HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Beamset 504H | Arakawa Chemical Industries, Ltd. | PUR, Unspecified | Beamset |
| Formolon® 676H | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Koylene ADL-CP AMR018N | Reliance Industries Limited | PP Random Copolymer | Koylene ADL-CP |
| LNP™ THERMOCOMP™ OF008E compound | SABIC Innovative Plastics | PPS | LNP™ THERMOCOMP™ |