Sipolprene® 55211
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SIPOL S.p.A |
| Trademark: | Sipolprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FCHIqF_Sipolprene-55211.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sipolprene® 55211 is an ether ester thermoplastic elastomer (TPC-ET), developed and manufactured by Sipol, with a nominal hardness of Shore D 54 and a rheological behaviour, which makes it suitable for injection moulding and extrusion processing. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183, ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption 1(23°C, 24 hr) | 2.1 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 54 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 39.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 570 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 132 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 215 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Immersion |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 301 TFE 15 | RTP Company | PC | RTP |
| RTP 800 TFE 2 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| Safron® R701-40RNA | Safripol (PTY) LTD | PP Random Copolymer | Safron® |
| NITRIFLEX PDC-7423 | NITRIFLEX | PVC+NBR | NITRIFLEX |
| Celcon® M450 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |