LUVOCOM® 94-8485 Datasheet,LDPE,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®94-8485 is a low density polyethylene material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. Typical application areas include: engineering/industrial accessories Tools container textile/fiber Automotive Industry

General Information
Uses	Thin wall parts Textile applications Engineering accessories Machine/mechanical parts Mould Application in Automobile Field Container Business equipment Food container Mold/Mold/Tool
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.57	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	> 50	g/10 min	ISO 1133
Molding Shrinkage	1.5 - 3.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	300	MPa	ISO 527-2
Tensile Stress (Break)	9.00	MPa	ISO 527-2
Tensile Strain (Yield)	20	%	ISO 527-2

Impact	Nominal Value	Test Method
Charpy Unnotched Impact Strength		ISO 179/1fU
-30°C	No Break	ISO 179/1fU
23°C	No Break	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	70.0	°C	UL 746B
Maximum operating temperature- Short Term	100	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+9	ohms	IEC 60167

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	80.0	°C	ISO 306/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+9	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	85	°C
Drying Time - Desiccant Dryer	2.0 - 3.0	hr
Rear Temperature	160 - 200	°C
Middle Temperature	170 - 220	°C
Front Temperature	180 - 240	°C
Nozzle Temperature	190 - 250	°C
Processing (Melt) Temp	230	°C
Mold Temperature	30 - 80	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	LDPE , Low Density Polyethylene
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	EWInml_LUVOCOM948485.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TECOLITE KM-757(J)	KYOCERA Chemical Corporation	Phenolic	TECOLITE
TOTAL Polypropylene PPC 3650	TOTAL Refining & Chemicals	PP Impact Copolymer	TOTAL Polypropylene
NuSil MED-4120	NuSil Technology	Rubber	NuSil
LNP™ STAT-KON™ OE002 compound	SABIC Innovative Plastics	PPS, Linear	LNP™ STAT-KON™
LNP™ STAT-KON™ PFD06 compound	SABIC Innovative Plastics	Nylon 6	LNP™ STAT-KON™