UBESTA 3030 JIX44
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E77Ltn_UBESTA-3030-JIX44.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBESTA 3030 JIX44 is a plasticized and impact modified PA12 grade. The applied low migration platicizer allows to use this grade especially in application where long term flexibility and excellent elastic memory characteristics are required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.5 | % | ISO 294-4 |
| Flow direction | 1.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 27 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 58 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 200 | % | ISO 527-2 |
| Flexural Modulus | 200 | MPa | ISO 178 |
| Flexural Stress | 10.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | No Break | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 40.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 170 | °C | ISO 3146 |
| CLTE - Flow | 1.9E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+10 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >200%Tensile Stress at Yield, ISO 527: >30 MPaAbrasion Loss, ISO 9352, CS-17, 1000 rev.: 30 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V221-80I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Latamid 66 H2 G/50-GWHF1 | LATI S.p.A. | Nylon 66 | Latamid |
| Latamid 66 H2PX-V0 | LATI S.p.A. | Nylon 66 | Latamid |
| Karina IVORY PVC COMPOUND 105907-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Capilene® CT 71 A | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |