VITAMIDE® TS20RD6369
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DqOHEn_VITAMIDE-TS20RD6369.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® TS20RD6369 is a Polyamide 66/6 Copolymer (Nylon 66/6) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Break | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact Strength | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 205 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 240 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 26 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arnite® T04 200 | DSM Engineering Plastics | PBT | Arnite® |
| Flontech® FT-CAF20-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| HAIPLEN H10 T8 HT | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Karina GRAY PVC COMPOUND 800-18/233-A-ERYB (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| AKROLEN® PP GFM 25/15 black 950088 (1415) | AKRO-PLASTIC GmbH | PP, Unspecified | AKROLEN® |