AGILITY™ 1002 Performance LDPE
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AGILITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DO3Bls_AGILITY-1002-Performance-LDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AGILITY™ 1002 Performance LDPE is a high pressure LDPE resin designed specifically to run at faster output rates on blown film lines in blends with LLDPE resins while maintaining bubble stability. This resin includes 2,000 ppm of anti-block to minimize blocking issues. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 0.565 | J | |
| Film Puncture Force | 22.2 | N | |
| Film Puncture Resistance | 2.48 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 26.5 | J/cm³ | ASTM D882 |
| TD | 51.3 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 243 | MPa | ASTM D882 |
| 2% secant, MD | 221 | MPa | ASTM D882 |
| 1% secant, TD | 301 | MPa | ASTM D882 |
| 2% secant, TD | 255 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 28.3 | MPa | ASTM D882 |
| TD : Yield | 13.0 | MPa | ASTM D882 |
| MD : Fracture | 29.6 | MPa | ASTM D882 |
| TD : Fracture | 16.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 110 | % | ASTM D882 |
| TD : Fracture | 430 | % | ASTM D882 |
| Dart Drop Impact | 75 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 290 | g | ASTM D1922 |
| TD | 95 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 109 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 51 | ASTM D2457 | |
| Haze | 10 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Type: DSB II Die Gap: 70 mil Melt Temperature: 398°F Output: 12 lb/hr/in. of die circumference Screw size: 3.5 in. Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 55 rpm Frost Line Height: 37 in. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Power Cable P-10040-CB | Polylink Polymers (India) Ltd. | TP, Unspecified | Polylink Power Cable |
| BP HDPE 9610 R BLK | Buckeye Polymers, Inc. | HDPE | BP |
| Caltex PP M910 | GS Caltex | PP Impact Copolymer | Caltex PP |
| MACOMASS PP MM-PP HI 84 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| Sylvin 8950-90 Grey 9415 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |