Di-Pak™ E-4901-10
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lFU4nH_Di-Pak-E-4901-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DI-PAK E-4901-2, E-4901-10, & E-4901-30 Low cost, easy to use, potting compounds with fast cycle times. Available in 3 speeds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.15 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 17 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 80 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 10.0 | min | ASTM D2971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Shock Test | Pass |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6530 | MPa | ASTM D638 |
| Tensile Strength | 3.17 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 41 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 9.28 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 | |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.22 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.8E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 1.67 | ||
| 100 kHz | 1.73 | ||
| Dissipation Factor (25°C, 100 kHz) | 9.0E-3 to 0.012 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 84, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 3500 | cP | ASTM D4878 |
| Demold Time (21°C) | 30 to 60 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC CRKA 01227 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Geon™ Vinyl Rigid Extrusion 87547 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Luxus SIS 109004 | Luxus Limited | SIS | Luxus SIS |
| Petlon R-Prime PET Clear 100 | Petlon Polymers Ltd | PET | Petlon R-Prime |
| Sylvin 4215-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |