LNP™ FARADEX™ ES003E compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DGauyB_LNP-FARADEX-ES003E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP FARADEX ES003E is a Polyetherimide resin containing 15% Stainless Steel Fibers. Added feature of this grade is: EMI/RFI Shielding. Also known as: LNP* FARADEX* Compound EMI-X ES-1003 EM Product reorder name: ES003E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4660 | MPa | ASTM D638 |
| -- | 4350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 105 | MPa | ASTM D638 |
| Yield | 99.0 | MPa | ISO 527-2/5 |
| Break 3 | 105 | MPa | ASTM D638 |
| Break | 98.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.8 | % | ASTM D638 |
| Yield | 4.1 | % | ISO 527-2/5 |
| Break 5 | 5.0 | % | ASTM D638 |
| Break | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4590 | MPa | ASTM D790 |
| -- 7 | 4310 | MPa | ISO 178 |
| Flexural Stress | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 34 | J/m | ASTM D256 |
| 23°C 8 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 9 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.60 | J | ASTM D3763 |
| -- | 1.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 190 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 194 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 180 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 177 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 4.0 | ohms | ASTM D257 |
| Shielding Effectiveness (2.50 mm) | 60 | dB | Internal Method |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tritan™ WX500 | Eastman Chemical Company | Copolyester | Tritan™ |
| AKROMID® A3 GF 30 5 black (2180) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ExxonMobil™ LLDPE LL 3201 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Elastron® D D400.A30.B | Elastron USA, Inc. | SBS | Elastron® D |
| Moplen HP520M | LyondellBasell Industries | PP Homopolymer | Moplen |