LNP™ THERMOCOMP™ UF00BAS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3LGGmv_LNP-THERMOCOMP-UF00BAS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UF00BAS is a compound based on Polyphthalamide containing 55% Glass Fiber. Added feature of this material is: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-100-11 A HS Product reorder name: UF00BAS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.64 | g/cm³ | |
| -- | 1.60 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19200 | MPa | ASTM D638 |
| -- | 18900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 246 | MPa | ASTM D638 |
| Break | 227 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.8 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 17300 | MPa | ASTM D790 |
| -- 5 | 15900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 314 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 338 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 82 | J/m | ASTM D256 |
| 23°C 7 | 9.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 290 | J/m | ASTM D4812 |
| 23°C 8 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.48 | J | ASTM D3763 |
| -- | 1.98 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 289 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 293 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 270 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 272 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 CC HI | RTP Company | PP, Unspecified | RTP |
| Sinvicomp SIZ7408A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| ADENE OMFB | A.D. Compound spa | PP Homopolymer | ADENE |
| Baoding 67I80 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Osterlene® HB3553A | Osterman & Company | HDPE | Osterlene® |