EPIMIX PBT GV0 10 NC
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPIMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DFnnQ8_EPIMIX-PBT-GV0-10-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EPIMIX PBT, Flame retardant, reinforced with 10% of glass fiber, heat stabilized, lubricated for injection moulding. EPIMIX PBT GV0 10 ,Halogenated , is used in all sectors of industry , compliance with RoHs derivatives, with rating UL94 V0 , offering a perfect balance of thermal and mechanical properties. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.52 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.1 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.40 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 10 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 82 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5100 | 4800 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 85.0 | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 2.0 | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 4500 | 4300 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 140 | 120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 6.0 | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 200 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 35195 B | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Sunny® PA66 HF200 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |
| Sylvin 8341-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Zhongfa ABS FR-765 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | ABS | Zhongfa |
| Osterlene® HE-3.8-2.9 | Osterman & Company | PS (HIPS) | Osterlene® |