SLOVAMID® 66 GF 50 HTS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PBm0dU_SLOVAMID-66-GF-50-HTS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66 for injection moulding, chemically reinforced with 50% glass fibre, heat stabilized and stabilized against hydrolysis. Used for cooling water systems in the automotive industry. Delivered in black colour. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.66 | % | |
| Flow | 0.47 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 235 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 13500 | MPa | ISO 178 |
| Flexural Stress | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 14 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 100 | kJ/m² | |
| 23°C | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 250 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ500 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Toler PE LL2420 | Toler Chemical, Inc | LLDPE | Toler PE |
| TOTAL Polypropylene PPC 7612 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| LUVOCOM® 50-7814/EM | Lehmann & Voss & Co. | PC | LUVOCOM® |
| PETILEN YY F 00756 | PETKIM Petrokimya Holding A.S. | HDPE | PETILEN |