Alathon® H6030
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CuUDYG_Alathon-H6030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON H 6030 is a homopolymer that provides enhanced processability, excellent stiffness and short molding cycles. Typical applications include thin wall and deep-draw. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.965 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Spiral Flow | 39.9 | cm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1080 | MPa | |
| 1% Secant | 931 | MPa | |
| Tensile Strength (Break) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.4 | % | ASTM D638 |
| Flexural Modulus 3 | ASTM D790 | ||
| -- | 1660 | MPa | |
| 1% Secant | 1540 | MPa | |
| 2% Secant | 1290 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | 280 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 82.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 117 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ WCD841U resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |
| Fiberfil® M-1492 BK223 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| HiPrene® ALC12B | GS Caltex | Nylon 6 | HiPrene® |
| OP - PSU 30GF | Oxford Polymers | PSU | OP - PSU |
| Durethan® BKV 50 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |