XYRON™ X1561
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CZaF0c_XYRON-X1561.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE 10% Filler reinforced Flame retardant V-0 Stiffness High, Warpage Low, |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 0.30 to 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 73.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 4.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 6.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-1 | ||
| 1.60 mm | V-0 | ||
| 2.50 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x2 mm |
| 2 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PP-B B 4920/507 TV 20 | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |
| Andur 8-5 APLS | Anderson Development Company | PUR-Ester/TDI | Andur |
| POLYCOMPO PE 2520F | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |
| Axiall PVC 8266 Natural 04 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| VALOX™ 865 resin | SABIC Innovative Plastics | PBT | VALOX™ |