LIHAN® A100
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5D8Ily_LIHAN-A100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN® A100 is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 8.0 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 1.4 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.0 to 1.4 | -- | % | ISO 62 |
| Water Content | 8.0 to 9.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 105 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 80.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 25 | 50 | % | ISO 527-2 |
| Flexural Modulus | 2700 | 1200 | MPa | ISO 178 |
| Flexural Stress | 100 | 45.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 3.4 | 10 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | DSC |
| CLTE - Flow | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength | 20 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | V-2 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLEM® 66 IM | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| Chiao Fu PA66/6 MB212GM45 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| Comai 408-2 NT | Comai Ltda | PP Copolymer | Comai |
| Desmovit® DP R 3914 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Softell TKG 300N G22452 | LyondellBasell Industries | PP Copolymer | Softell |