RTP 285 TFE 10 SI 2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CXHkn0_RTP-285-TFE-10-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 0.050 | % | ASTM D955 |
| 6.35mm, injection molding | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 20700 | MPa | ASTM D638 |
| Tensile Strength | 200 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 1.6 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 17900 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 303 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 750 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 249 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 274 - 293 | °C | |
| Middle Temperature | 274 - 293 | °C | |
| Front Temperature | 274 - 293 | °C | |
| Mold Temperature | 66.0 - 107 | °C | |
| Injection Pressure | 69.0 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 HI 30 GF BLK | RTP Company | Nylon 66 | RTP |
| Shin-Etsu Elastomer KE-661U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| BorSafe™ ME3440-D | Borealis AG | MDPE | BorSafe™ |
| Celstran® PA6-GF30-01 | Celanese Corporation | Nylon 6 | Celstran® |
| POCAN® B 4235 Z 000000 | LANXESS Corporation | PBT | POCAN® |