| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SEKISUI Polymer Innovations, LLC |
| Trademark: | Allen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | COgsAO_Allen-FR3030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EFG is a polycarbonate and ABS blend with very high impact properties, stiffness, heat resistance and flame retardant V-0 rating. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 68.9 | MPa | ASTM D638 |
| Flexural Modulus | 2790 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -40°C | 160 | J/m | |
| 23°C | 750 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 106 | °C | ASTM D648 |
| Vicat Softening Temperature | 113 | °C | ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | V-0 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss - 60° | 85 | % | ASTM D923 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC B3 HF UV CRLA010 PC306 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Maxelast® F02-138A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| VICOTE® 701 | Victrex plc | PEEK | VICOTE® |
| Elastocon® 8088BL | Elastocon TPE Technologies | TPE | Elastocon® |
| Karina WHITE MINERAL CONC. MBU -E 10/0085-IE | Karina Ind. e Com. de Plásticos Ltda | EVA | Karina |