Queo™ 1001

Category:	Plastomer , Ethylene-based Plastomer
Manufacturer:	Borealis AG
Trademark:	Queo™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	C4hdqz_Queo-1001.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Queo™ 1001 is an ethylene based octene plastomer produced using a metallocene catalyst in a solution polymerisation process.

Queo 1001 is a versatile blend partner for other polyolefins in film, extrusion and moulding applications, offering :

Unrivalled sealing properties

Outstanding toughness, puncture resistance and low temperature impact strength

Excellent polyolefin compatibility

Flexibility

Excellent environmental stress cracking resistance

Low amount of extractables

High clarity

Applications:
Demonstrated applications include :

Seal layers in lamination and flexible barrier films

High strength flexible films

Flexible low voltage insulation

Blow moulded articles

Flexible automotive boots and bellows

Soft foams

Additives:

Queo 1001 contains processing stabilizers.

General Information
Additive	Unspecified Stabilizer
Features	Good Flexibility Good Toughness High Clarity High ESCR (Stress Crack Resist.) High Strength Low Temperature Impact Resistance Puncture Resistant
Uses	Automotive Applications Foam Seals
Processing Method	Blown Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.910	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.1	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance	> 1000	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	49		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	35.0	MPa	ISO 527-2/5A
Tensile Strain (Break)	750	%	ISO 527-2/5A
Flexural Modulus	132	MPa	ISO 178

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD	90.0	MPa	ASTM D882
Dart Drop Impact (Blown Film)	> 22	g	ASTM D1709

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength (23°C)	No Break		ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	93.0	°C	ISO 306/A
Melting Temperature (DSC)	106	°C	ISO 11357

Optical	Nominal Value	Unit	Test Method
Gloss (45°)	81		ASTM D2457
Haze	2.0	%	ASTM D1003A

Additional Information	Nominal Value	Unit	Test Method
Puncture Resistance	28.0	J/cm	Internal Method
Sealing Initial Temperature	87	°C	ASTM F88

Resin Grade	Manufacturer	Category	Trademark
MARPOL® Homo 20.NA	Marco Polo International, Inc.	PP Homopolymer	MARPOL® Homo
SCANFILL BOTTLE BY45C2	Polykemi AB	HDPE	SCANFILL
Trademark PP PPR1200MA	Trademark Plastics Corporation	PP Random Copolymer	Trademark PP
Hanwha Total PP SI81R	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, Unspecified	Hanwha Total PP
Purell RP271G	LyondellBasell Industries	PP Random Copolymer	Purell