Order Products : sales@su-jiao.com
LNP™ STAT-KON™ KEP33 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BTvegq_LNPSTATKONKEP33compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* KEP33 is a compound based on Acetal resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound KCL-4533 Product reorder name: KEP33 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.070 - 0.090 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.32 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10200 | MPa | ASTM D638 |
| -- | 10200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 77.5 | MPa | ASTM D638 |
| Fracture | 74.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.1 | % | ASTM D638 |
| Fracture | 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7150 | MPa | ASTM D790 |
| -- | 8270 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 114 | MPa | ASTM D790 |
| -- | 107 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.36 | ASTM D3702 Modified | |
| With Self-Static | 0.31 | ASTM D3702 Modified | |
| Wear Factor - Washer | 202 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 3.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D4812 |
| 23°C 3 | 17 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.20 | J | ASTM D3763 |
| -- | 4.02 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 66.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 155 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 10 - 1.0E+4 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIH7007A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Small Boss STPR002 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | SBS | Small Boss |
| Neopor® F 4 speed | BASF Corporation | PS (EPS) | Neopor® |
| INEOS PP 101-GB08 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| Petrothene® GA837091 | LyondellBasell Industries | LMDPE | Petrothene® |