Lotrène® LLDPE Q1018N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | QATOFIN Company Limited |
| Trademark: | Lotrène® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B7nkpU_Lotr-ne-LLDPE-Q1018N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lotrène® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties. Lotrène® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks, refuse, tunnel films, mulching films… |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 40 µm, blown film | 215 | MPa | ASTM D882 |
| 1% secant, TD : 40 µm, blown film | 245 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 40 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 40 µm, blown film | 38.0 | MPa | ASTM D882 |
| TD : Broken, 40 µm, blown film | 33.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 40 µm, blown film | 800 | % | ASTM D882 |
| TD : Broken, 40 µm, blown film | 850 | % | ASTM D882 |
| Dart Drop Impact 1(40 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, blown film | 280 | g | ASTM D1922 |
| TD : 40 µm, blown film | 480 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Peak Crystallization Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 2 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 180 - 220 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Cylinder Zone 5 Temp. | 180 - 220 | °C | |
| Melt Temperature | 200 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 2:1 to 3:1Die gap: >1.8 mm |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 127618 R | RTP Company | PLA+PC | RTP |
| Karina IVORY PVC COMPOUND 550D35/ 1-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS EFR268 | AD majoris | PP, Unspecified | MAJORIS |
| LUVOCOM® 6/CF/30 | Lehmann & Voss & Co. | Nylon 12 | LUVOCOM® |
| LEXAN™ XHT5146 resin | SABIC Innovative Plastics | PC | LEXAN™ |