LNP™ THERMOCOMP™ RC004SXC compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B5PY1K_LNP-THERMOCOMP-RC004SXC-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RC004SXC is a compound based on PA66 resin containing Carbon Fiber. Added features include: Electrically Conductive, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RC004SXC Product reorder name: RC004SXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 10500 | MPa | ISO 178 |
| Flexural Stress | 269 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 250 | °C | ISO 75-2/Af |
| CLTE - Flow (23 to 60°C) | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EMERGE™ PC 8430-22 | Trinseo | PC | EMERGE™ |
| LNP™ THERMOCOMP™ KZ001L compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |
| Lucent PP TPP-330 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| TECHNYL® C 52G2 MV25 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Sylvin 9067F4 Red 6253 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |