SOLLAMID A 2700 - A 2730 FV 25
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Krisoll Resinas Plásticas Ltda. |
| Trademark: | SOLLAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AssnDw_SOLLAMID-A-2700---A-2730-FV-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLLAMID A 2700 - A 2730 FV 25 is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Latin America. Primary attribute of SOLLAMID A 2700 - A 2730 FV 25: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.32 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.35 to 0.55 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ASTM D570 |
| Heat Stability | 120 to 130 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 122 | 110 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8200 | 6000 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 150 | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.5 | 5.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6500 | 4000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 226 | 120 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Unnotched Izod Impact Strength (23°C) | 10 | 15 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | > 200 | -- | °C | |
| 1.8 MPa, Unannealed | > 240 | -- | °C | |
| Melting Temperature | 250 to 260 | -- | °C | |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7693B | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SCHULAFORM® 9 A TF 20 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| BCC Resins BC 9040T | BCC Products Inc. | Silicone | BCC Resins |
| Geon™ Vinyl Flexible R354AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Rotuba CAB B9024 (11% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |