Plenco 02408 (Injection)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Adg0Sr_Plenco-02408-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 02408 is a general purpose, organic filled phenolic molding compound, offering excellent cosmetic characteristics and improved electrical strength properties. UL recognized under component file E40654. 02408 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.36 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8400 | MPa | ASTM D638 |
| Tensile Strength | 58.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 6940 | MPa | ASTM D790 |
| Flexural Strength | 76.5 | MPa | ASTM D790 |
| Compressive Strength | 213 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18.8 | J/m | ASTM D256 |
| Notched Izod Impact | 18 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 158 | °C | ASTM D648 |
| Continuous Use Temperature | 200 | °C | ASTM D794 |
| CLTE - Flow | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.7E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 10 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.047 | ASTM D150 | |
| Arc Resistance | 134 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.00 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 33%Heat Resistance, ASTM D794: 200°CDrop Ball Impact, PLENCO Method: 100 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 66.0 - 82.0 | °C | |
| Front Temperature | 82.0 - 99.0 | °C | |
| Processing (Melt) Temp | 104 - 115 | °C | |
| Mold Temperature | 165 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytech & Net VC810 | Polytech & Net Gmbh | EVA | Polytech & Net |
| Somos® NanoTool | DSM Somos® | Unspecified | Somos® |
| AKROMID® B3 GF 40 1 natural (2466) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Plexiglas® V052i | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| POLYLAC® PA-757GJ08 | CHI MEI CORPORATION | ABS | POLYLAC® |