KOPA® KN333G20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5A0BvK_KOPAKN333G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA®KN333G20 is a polyamide 66 (nylon 66) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Latin America, Europe or Asia Pacific. KOPA®KN333G20 applications include electrical/electronic applications, engineering/industrial accessories and the automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 162 | MPa | ASTM D638 |
| 23°C | 140 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 7.0 | % | ASTM D638 |
| Fracture, 23°C | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5980 | MPa | ASTM D790 |
| 23°C | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 226 | MPa | ASTM D790 |
| 23°C | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 250 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 240 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80 - 100 | °C | |
| Drying Time - Desiccant Dryer | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 275 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPA1260 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| MTEGRITY™ PP Homopolymer PP204 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| Chiao Fu PP PP212GM20 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Chiao Fu PBT PBT819B15 NAT | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| Pebax® MV 3000 SP 01 | Arkema | PEBA-Ether | Pebax® |