Starex LX-0957
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AcoQl4_Starex-LX-0957.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex LX-0957 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 | g/cm³ | ASTM D792 |
| -- | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.21 to 0.29 | % | |
| Across Flow : 3.20 mm | 0.21 to 0.29 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 111 | ASTM D785 | |
| R-Scale | 114 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 45.0 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2/5 |
| Break 3 | 38.0 | MPa | ASTM D638 |
| Break | 35.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 31 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 2600 | MPa | ASTM D790 |
| -- 6 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 69.0 | MPa | ASTM D790 |
| -- 8 | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 170 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 150 | J/m | ASTM D256 |
| 23°C 10 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 94.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.20 to 1.32 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Calprene® 487 | Dynasol Elastomers | SBS | Calprene® |
| Lupoy® EF1006F | LG Chem Ltd. | PC | Lupoy® |
| Lupoy® GN5007FL | LG Chem Ltd. | PC+ABS | Lupoy® |
| Lushan VB760 | Guangzhou Lushan New Materials Co., Ltd | PE, Unspecified | Lushan |
| ULTEM™ 2312EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |