Ultramid® B3WG6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AGFEhn_Ultramid-B3WG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade. Applications Typical applications include automotive manifolds and pedals. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 50.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| Saturation | 6.6 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.6 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.1 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | 6200 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 179 | -- | MPa | ASTM D638 |
| Break, 23°C | 185 | 115 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.3 | -- | % | ASTM D638 |
| Break, 23°C | 3.5 | 8.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 8280 | -- | MPa | ASTM D790 |
| 23°C | 8600 | 5000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 270 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 15 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² | |
| Notched Izod Impact | ||||
| -40°C | 110 | -- | J/m | ASTM D256 |
| 23°C | 130 | -- | J/m | ASTM D256 |
| 23°C | 15 | 20 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 1.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 2.3E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 90.0 | -- | °C | |
| 3.00 mm | 95.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+13 | 1.0E+10 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | 6.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.023 | 0.22 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E 398 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Fiberfil® PP-60/TC/13 BL8860 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Keysor PVC KYFF | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| Lucent PP PPC-320 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| Sylvin 9848-75FR Grey 9361 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |