LNP™ THERMOCOMP™ LF006 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Nz7pQ_LNP-THERMOCOMP-LF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* LF006 is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound LF-1006 Product reorder name: LF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.54 | g/cm³ | ASTM D792 |
| -- | 1.53 | g/cm³ | ISO 1183 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13200 | MPa | ASTM D638 |
| -- | 13100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 176 | MPa | ASTM D638 |
| Break | 175 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.0 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10800 | MPa | ASTM D790 |
| -- | 12700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 246 | MPa | ASTM D790 |
| -- | 264 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 880 | J/m | ASTM D4812 |
| 23°C 3 | 57 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 13.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | > 299 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | > 240 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | > 299 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | > 240 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.780 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIZ7408A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| SPI HDPE20 | Service Polymers, Inc. | HDPE | SPI |
| DILAMID® 6 FVT 30 NAT A | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| K-vinyl 20 A 75 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| LNP™ THERMOCOMP™ LC008E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |