Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.

General Information
Filler / Reinforcement	Long glass fiber, 60% filler by weight
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.71	g/cm³	ISO 1183
Molding Shrinkage	0.050 - 0.15	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	15900	MPa	ISO 527-1
Tensile Strength (Yield)	255	MPa	ISO 527-2
Tensile Elongation ²(Break)	2.0 - 3.0	%	ISO 527-2
Flexural Modulus	19300	MPa	ISO 178
Flexural Strength (Yield)	362	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm, Injection Molded)	480	J/m	ISO 180
Unnotched Izod Impact	1700	J/m	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	114	°C	ISO 75-2/A

Injection	Nominal Value	Unit
Drying Temperature	90.0	°C
Drying Time	8.0 - 12	hr
Processing (Melt) Temp	230 - 250	°C
Mold Temperature	80.0	°C

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C.

Note Message
1 .	Type 1, 5.1 mm/min
2 .	Type 1, 5.1 mm/min

Resin Grade	Manufacturer	Category	Trademark
Vydyne® R515H	Ascend Performance Materials Operations LLC	Nylon 66	Vydyne®
Bapolene® 3255	Bamberger Polymers, Inc.	HDPE	Bapolene®
Alkathene® WNC199	Qenos Pty Ltd	LLDPE	Alkathene®
Iupilon® EGW2020DR 9005	Mitsubishi Engineering-Plastics Corp	PC	Iupilon®
Polimid A SG LDM	Poliblend S.p.a.	Nylon 66	Polimid A