AZDEL™ C321B02N Datasheet,PP Alloy,Azdel, Inc.-SHANGHAI SUSHENG

Message
Azdel® C321B02N is a chopped fiber material based on random oriented long chopped glass fiber mat (paper making process). This polypropylene composite material features high flow properties and a very homogeneous fiber distribution. This material is typically used for standard semi-structural, thin walled applications.

General Information
Filler / Reinforcement	Long glass fiber, 32% filler by weight
Features	High liquidity
Uses	Laminate
Forms	Sheet
Processing Method	Compression molding

Physical	Nominal Value	Unit	Test Method
Density	1.17	g/cm³	ISO 1183

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4800	MPa	ISO 527-2
Tensile Stress (Yield)	85.0	MPa	ISO 527-2
Tensile Strain (Break)	2.6	%	ISO 527-2
Flexural Modulus	4400	MPa	ISO 178
Flexural Stress	135	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength	85	kJ/m²	ISO 179/2fnU
Multi-Axial Instrumented Impact Energy			ISO 6603-2
4.00, energy to power peak	17.0	J	ISO 6603-2
4.00, total impact penetration energy	45.0	J	ISO 6603-2
Multi-Axial Instrumented Impact Peak Force (4.00 mm)	5500	N	ISO 6603-2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	160	°C	ISO 75-2/A
Melting Temperature (DSC)	166	°C	ISO 3146

Additional Information
Mass Per Unit Area, Azdel Test Method: 5.500 kg/m²Thickness, Azdel Test Method: 4.9 mmDensity, ISO 1183 Test Method: 1.13 g/cm³Density, ISO 1183 Test Method, Molded Plaque: 1.17 g/cm³Recrystallizing Temperature, ISO 3146 Test Method: 115 °CCTLE, Azdel Test Method, -30°C to 0°C, 3mm: 4.8e-5 1/°CCTLE, Azdel Test Method, 0°C to 120°C, 3mm: 3.6e-5 1/°CBlank Heat Parameters-Internal Temperature: 190 to 215°C-Surface Temperature: 205 to 220°C-Typical Heating Time for IR-System: 180 to 240°C-Typical Heating Time for Hot Air System: 240 to 480°CMould Temperature: 30 to 90°CMoulding Preasure: 150 to 250 barMinimum Pressing Speed: 20 mm/secTotal Cycle Time: 30 to 90 sec

Additional Information

Mass Per Unit Area, Azdel Test Method: 5.500 kg/m²Thickness, Azdel Test Method: 4.9 mmDensity, ISO 1183 Test Method: 1.13 g/cm³Density, ISO 1183 Test Method, Molded Plaque: 1.17 g/cm³Recrystallizing Temperature, ISO 3146 Test Method: 115 °CCTLE, Azdel Test Method, -30°C to 0°C, 3mm: 4.8e-5 1/°CCTLE, Azdel Test Method, 0°C to 120°C, 3mm: 3.6e-5 1/°CBlank Heat Parameters-Internal Temperature: 190 to 215°C-Surface Temperature: 205 to 220°C-Typical Heating Time for IR-System: 180 to 240°C-Typical Heating Time for Hot Air System: 240 to 480°CMould Temperature: 30 to 90°CMoulding Preasure: 150 to 250 barMinimum Pressing Speed: 20 mm/secTotal Cycle Time: 30 to 90 sec

Category:	PP Alloy , Polypropylene Alloy
Manufacturer:	Azdel, Inc.
Trademark:	AZDEL™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	9MHfFx_AZDEL-C321B02N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 4701 FR	RTP Company	PTT	RTP
RTP 400 HI TFE 10	RTP Company	PS (HIPS)	RTP
Luxus TPE 108004	Luxus Limited	TPE	Luxus TPE
KMI PP KM-815IB	KMI Group, Inc.	PP Impact Copolymer	KMI PP
Sylvin 9077-80 Red 604	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin