TAROLOX 111 G7 DX02
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Gauhv_TAROLOX-111-G7-DX02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PET glass fiber reinforced 35%, self extinguishing V0 without PBDE/PBDF, high temperature resistance, good flow, very good mechanical, thermal and electrical properties, low moisture absorption, good dimensional stability. Product must be dried before moulding. UL94 V0 approved all colours at 1,5 mm - V2 at 0,75 mm. UL 746B under testing. Available: all colors, heat stabilized (H), release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.30 | % | |
| Across Flow | 0.60 to 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570, ISO 62 |
| Granule Humidity | < 0.030 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 12000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 190 | MPa | ISO 178 |
| Break | 190 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 243 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 246 | °C | ISO 306/B50, ASTM D1525 1 |
| Melting Temperature | 256 | °C | ASTM D211, ISO 121 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 100 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SP660 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Globalene® SF7351 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| InnoTooling™ IE-9060 | Innovative Polymers, Inc. | TSU | InnoTooling™ |
| PLUSTEK PA303G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| ESTOPLAST XU 6250BB01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |